STAT-KON DEI13F Compound. Polycarbonate 15% Carbon Fiber & 2% Silicone

Wear Resistant, Electrically Conductive, High Strength, High Stiffness

LNP™ STAT-KON™ DEI13F Compound is a Polycarbonate Resin with 15% Carbon Fiber & 2% Silicone Reinforced. Improved Structural Performance

The Polycarbonate Compound Surface Resistivity = 1.E+02 – 1.E+06 Ω.

STAT-KON™ DEI13F Featured such as : -
- Wear Resistant
- High Flow
- UL94 Rated
- Electrically Conductive
- High Stiffness
- High Strength

Applications Examples

- Electronic Components
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ DEI13F Resin has a Flexural Modulus of 9790 MPa. 2 mm/min ISO 178

STAT-KON™ DEI13F Resin offers a Tensile Strain, Break, 5 mm/min of 1.8%. ISO 527

SABIC LNP™ STAT-KON™ DEI13F compound offer HDT, 1.82 MPa of 142°C

LNP™ STAT-KON™ DEI13F Compound Resin has 0.1 ~ 0.3% Shrinkage, Along Flow

STAT-KON® DEI13F Compound are UL94 - HB @ 1.5 mm