STAT-KON DX13320C Compound. Polycarbonate, 20% Carbon Fiber Reinforced

Clean Compounding Technology, Low C18-C40 Hydrocarbons & Good Flow

LNP™ STAT-KON™ DX13320C Compound is a Polycarbonate Resin with 20% Carbon Fiber Reinforced

The Compound Surface Resistivity = 5.E+03 – 5.E+05 Ω. Low C18 ~ C40 Hydrocarbons and UL94 Rated

The Compounding is made from Clean Compounding Technology. Feature Low level of Volatiles and Ionics Contamination from Nitrates, Chlorides and Sulfates. It Reduces the Potential of Wafer Damages while promoting more Accurate and Reliable Data Reading

STAT-KON™ DX13320C Featured such as : -
- Electrically Conductive
- High Stiffness
- High Strength
- Super Strong (Carbon Fiber Reinforced)
- High Modulus
- High Heat Resistance
- Low Ionics
- Low Outgassing

Applications Examples

- Electronic Components
- Computer Tablets
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ DX13320C Resin has a Flexural Modulus of 11600 MPa. 2 mm/min ISO 178

STAT-KON™ DX13320C Resin offers a Tensile Strain, Break, 5 mm/min of 1.9%. ISO 527

SABIC LNP™ STAT-KON™ DX13320C compound offer HDT, 1.82 MPa of 117°C

LNP™ STAT-KON™ DX13320C Compound Resin has 0.1 ~ 0.2% Shrinkage, Along Flow

STAT-KON® DX13320C Compound are UL94 - HB @ 1.0 mm ~ 3.0 mm