STAT-KON EX01407C Compound. Polyetherimide Resin Carbon Fiber & PTFE

Clean Compounding Technology, High Stiffness & Wear Resistance

LNP™ STAT-KON™ EX01407C Compound is a Polyetherimide Resin with Carbon Fiber & PTFE Reinforced

The Compound Surface Resistivity = 1.E+02-1.E+06 Ω.

The Compounding is made from Clean Compounding Technology. Feature Low level of Volatiles and Ionics Contamination from Nitrates, Chlorides and Sulfates. It Reduces the Potential of Wafer Damages while promoting more Accurate and Reliable Data Reading

STAT-KON™ EX01407C Featured such as : -
- Electrically Conductive
- High Stiffness
- High Strength
- High Heat Resistance
- Low Ionics
- Low Outgassing
- Clean Compounding Technology Produced

Applications Examples

- Electronic Components
- Computer Tablets
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ EX01407C Resin has a Flexural Modulus of 9640 MPa. 2 mm/min ISO 178

STAT-KON™ EX01407C Resin offers a Tensile Strain, Break, 5 mm/min of 89%. ISO 527

SABIC LNP™ STAT-KON™ EX01407C compound offer HDT, 1.82 MPa of 209°C

LNP™ STAT-KON™ EX01407C Compound Resin has 0.55% Shrinkage, Along Flow

STAT-KON® EX01407C Compound are Non UL94 Listed