STAT-KON EX99689C Compound. Polyetherimide Resin 10% Carbon Fiber

Clean Compounding Tech, Electrically Conductive, Stiffness & High Heat

LNP™ STAT-KON™ EX99689C Compound is a Polyetherimide Resin with 10% Carbon Fiber Reinforced

The Compound Surface Resistivity = 1.E+02-1.E+06 Ω. UL94 Rated

The Compounding is made from Clean Compounding Technology. Feature Low level of Volatiles and Ionics Contamination from Nitrates, Chlorides and Sulfates. It Reduces the Potential of Wafer Damages while promoting more Accurate and Reliable Data Reading

STAT-KON™ EX99689C Featured such as : -
- Electrically Conductive
- High Stiffness
- High Strength
- Super Strong (Carbon Fiber Reinforced)
- High Heat Resistance
- Clean Compounding Technology Produced

Applications Examples

- Electronic Components
- Computer Tablets
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ EX99689C Resin has a Flexural Modulus of 7700 MPa. 2 mm/min ISO 178

STAT-KON™ EX99689C Resin offers a Tensile Strain, Break, 5 mm/min of 1.2%. ISO 527

SABIC LNP™ STAT-KON™ EX99689C compound offer HDT, 1.82 MPa of 205°C

LNP™ STAT-KON™ EX99689C Compound Resin has 0.2 % Shrinkage, Along Flow

STAT-KON® EX99689C Compound are UL94 - V0 @ 0.35 mm