STAT-KON OE008A Compound. Polyphenylene Sulfide with 40% Carbon Fiber

Extreme Rigidity, High Temperature Resistance and Chemical Resistance

LNP™ STAT-KON™ OE008A Compound is a Polyphenylene Sulfide with 40% Carbon Fiber Reinforced. Extreme Rigidity

The Compound Surface Resistivity = 1.E+01-1.E+03 Ω. UL94 Rated

The PPS Compound offers Balance of Properties, such as High Temperature Resistance, Chemical Resistance, Flowability, Dimensional Stability and Electrical Characteristics

STAT-KON™ PPS OE008A Featured such as : -
- Electrically Conductive
- Self-Extinguishing without adding Flame Retardants.
- Good Chemical Resistance
- Good Heat Resistance
- High Rigidity
- Low Moisture Absorption
- Very Good Thermal Stability

Applications Examples

- Electronic Components
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ OE008A Resin has a Flexural Modulus of 30300 MPa. 2 mm/min ISO 178

STAT-KON™ OE008A Resin offers a Tensile Strain, Break, 5 mm/min of 0.7%. ISO 527

SABIC LNP™ STAT-KON™ OE008A compound offer HDT, 1.82 MPa of -°C

LNP™ STAT-KON™ OE008A Compound Resin has 0.1 ~0.3% Shrinkage, Along Flow

STAT-KON® OE008A Compound are UL94 - V0 @ 1.00 mm ~ 1.10 mm