STAT-KON RX04031 Polyamide 6/6 10% Carbon Fiber and 35% Glass Fiber

Non-Brominated, Non-Chlorinated Flame Retardant & Easy Molding Grade

LNP™ STAT-KON™ RX04031 Compound is a Nylon 6/10 with 10% Carbon Fiber & 35% Glass Fiber Reinforced. Electrically Conductive with Non-Brominated, Non-Chlorinated Flame Retardant & Easy Molding Formulation

The Compound Surface Resistivity = 1.E+03 - 1.E+04 Ω.

The Polyamide 6/6 (PA6/6) Compound offers Chemical Resistance to Hydrocarbons & Better Stiffness Formulated

STAT-KON™ RX04031 Nylon 6/6 Featured such as : -
- Electrically Conductive
- Excellent Strength
- High Heat Tolerance
- Good Abrasion and Wear Resistance
- Chemical Resistance to Hydrocarbons
- High Stiffness
- Wear Resistance and Lubricity
- Good Processability

Applications Examples

- Electronic Components
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ RX04031 Resin has a Flexural Modulus of 15000 MPa. 2 mm/min ISO 178

STAT-KON™ RX04031 Resin offers a Tensile Strain, Break, 5 mm/min of 2%. ISO 527

SABIC LNP™ STAT-KON™ RX04031 compound offer HDT/Af 64 mm, 1.8 MPa of 218°C

LNP™ STAT-KON™ RX04031 Compound Resin has 0.2% Shrinkage, Along Flow

STAT-KON® RX04031 Compound are UL94 - V0 @ 0.80 mm ~ 3.00 mm