POLYLAC PA-727 is an ABS Resin Dedicated for Ease of Electroplating

High Impact Strength, High Gloss Finishing & High Rigidity Features

POLYLAC™ PA-727 is a Electroplating Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties.

The Unique POLYLAC™ PA-727 Resin offers Ease of Metal Coating Adhesion and Uniform Bonding of Electroplating. Therefore, the Finishing will Rresult in a High Quality, Durable Finish that meets the Desired Specifications for the Application such as Automotive Parts

POLYLAC™ PA-727 has Melt Flow Index of 19 ml/10 min ( Based on ISO 1133 Test Method )

POLYLAC™ PA-727 Featured such as : -
- High Gloss Finishing
- High Rigidity
- High Impact Strength
- Ease of Electroplating

CHIMEI POLYLAC™ PA-727 Compound Resin has 0.4 ~ 0.7% Mold Shrinkage

POLYLAC™ PA-727 Resin has a Flexural Modulus of 2 GPa. 2 mm/min ISO 178

POLYLAC™ PA-727 Resin offers a Tensile Elongation 50 mm/min of 80%. ISO 527

CHIMEI POLYLAC™ PA-727 compound offer HDT,75/A, 1.82 MPa Unannealed of 83°C

CHIMEI POLYLAC™ PA-727 offer 25 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-727 ABS Resin are UL94 - HB@1.5 mm ~ 3.0 mm