POLYLAC PA-764B is an ABS Resin, Good Flame Retardant Opaque Grade

Impact Strength Plastic with High Heat Resistance & UL94-V0@1.5 mm

POLYLAC™ PA-764B is a FR Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties. Good Flow

The Good Weather Ability, Flame Retardant Series of POLYLAC™ PA-764B Opaque Colored, High Heat Resistance. Flame retardants are added to Reduce their Flammability and Slow Down or Prevent the Spread of Fire for High Power Electrical Parts. UL94 2.5mm ~ 3.0 mm 5VA

POLYLAC™ PA-764B has Melt Flow Index of 26 ml/10 min ( Based on ISO 1133 Test Method )

POLYLAC™ PA-764B Featured such as : -
- Good Weather Ability
- Opaque Colored
- High Impact Strength
- Flame Retardant
- High Heat Resistance

CHIMEI POLYLAC™ PA-764B Compound Resin has 0.3 ~ 0.6% Mold Shrinkage

POLYLAC™ PA-764B Resin has a Flexural Modulus of 1.8 GPa. 2 mm/min ISO 178

POLYLAC™ PA-764B Resin offers a Tensile Elongation 50 mm/min of 10%. ISO 527

CHIMEI POLYLAC™ PA-764B compound offer HDT,75/A, 1.82 MPa Unannealed of 83°C

CHIMEI POLYLAC™ PA-764B offer 14 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-764B ABS Resin are UL94 - V0@2.5 mm ~ 3.0 mm