POLYLAC PA-777E is a Ultra High Heat, Best Thermal Stability ABS Resin

Moderate Impact Strength for Demanding Appliances and UL94-HB Rating

POLYLAC™ PA-777E is a High Heat Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties.

The Ultra Super High Heat POLYLAC™ PA-777E Resin offers Highest Thermal Stability and Mechanical Properties. It can Withstand Continuous use at High Temperatures without Significant Deformation or Loss of Properties. Meanwhile, it also has Excellent Dimensional Stability, Chemical Resistance, and Surface Finish, which makes it an Ideal Material for High Heat Appliances such as Hair Dryers, Toasters, Iron Casing, Water Heater or Coffee Makers.

POLYLAC™ PA-777E Resin Moderate Impact Strength Ensures that the Appliance Components Made from it can Withstand the Rigors of Daily Use, while its Heat Resistance enables Them to Operate Reliably under Extreme Conditions. Additionally, its Excellent Flow Properties make it Easy to Mold Complex Shapes with Intricate Details, allowing for Greater Design Flexibility.

It has Melt Flow Index of 4.5 ml/10 min ( Based on ISO 1133 Test Method ).

POLYLAC™ PA-777E Featured such as : -
- Good Gloss
- Good Rigidity
- Ultra High Heat
- Moderate Impact Strength

CHIMEI POLYLAC™ PA-777E Compound Resin has 0.3 ~ 0.6% Mold Shrinkage

POLYLAC™ PA-777E Resin has a Flexural Modulus of 2.3 GPa. 2 mm/min ISO 178

POLYLAC™ PA-777E Resin offers a Tensile Elongation 50 mm/min of 30%. ISO 527

CHIMEI POLYLAC™ PA-777E compound offer HDT,75/A, 1.82 MPa Unannealed of 101°C

CHIMEI POLYLAC™ PA-777E offer 13 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-777E ABS Resin are UL94 - HB@1.5 mm ~ 3.0 mm